AJMB Avicenna Journal of Medical Biotechnology 2008-2835 2008-4625 Avicenna Research Institute AJMB-3-195 Original Article An Enhancing Effect of Gold Nanoparticles on the Lethal Action of 2450 MHz Electromagnetic Radiation in Microwave Oven Mollazadeh-Moghaddam Kamyar 1 Moradi Bardia Varasteh 2 Dolatabadi-Bazaz Reza 3 Shakibae Mojtaba 4 Shahverdi Ahmad Reza 2 * Students' Scientific Research Center, Tehran University of Medical Sciences, Tehran, Iran Department of Pharmaceutical Biotechnology and Biotechnology Research Center, Faculty of Pharmacy, Tehran University of Medical Sciences, Tehran, Iran Department of Medicinal Chemistry, Faculty of Pharmacy, Tehran University of Medical Sciences, Tehran, Iran Department of Pharmacognosy and Biotechnology, School of Pharmacy, Pharmaceutics Research Center, Kerman University of Medical Sciences, Kerman, Iran Corresponding author: Ahmad Reza Shahverdi, Ph.D., Department of Pharmaceutical Biotechnology and Biotechnology Research Center, Faculty of Pharmacy, Tehran University of Medical Sciences, Tehran, Iran. Tel: +98 21 6482706. Fax: +98 21 66461178. E-mail: shahverd@sina.tums.ac.ir October-December 2011 3 4 195 200 19 10 2011 12 12 2011 Copyright © 2011 Avicenna Research Institute 2011

This work is licensed under a Creative Commons Attribution-NonCommercial 3.0 Unported License which allows users to read, copy, distribute and make derivative works for non-commercial purposes from the material, as long as the author of the original work is cited properly.

Today, there is an increasing interest in the use of metal nanoparticles in health sciences. Amongst all nanoparticles, the gold nanoparticles have been known to kill the cancer cells under hyperthermic condition by near-infrared frequency electromagnetic waves. On the other hand, although there are different physiochemical methods for disinfection of microbial pollution, however applications of irradiated gold nanoparticles against microorganisms have not yet been investigated. In this study, gold nanoparticles were prepared using D-glucose and characterized (particle size <26 nm). In the next step, the enhancing effect of the non toxic level of gold nanoparticles (50 µg/mL) on the antimicrobial activity of 2450 MHz electromagnetic radiation generated at a microwave oven operated at low power (100 W), was investigated by time-kill course assay against Staphylococcus aureus (S.aureus) ATCC 29737. The results showed that application of gold nanoparticles can enhance the lethal effect of low power microwave in a very short exposure time (5 s).

Antimicrobial effect Electromagnetic radiation Gold nanoparticles Microwave Staphylococcus aureus
Introduction

Researchers demonstrated that electromagnetic waves kill the microorganisms by changing the vibration frequency of the molecules (1). Although it has been established that high frequency electromagnetic waves have enough power to kill microorganisms, but these electromagnetic waves have many side effects that impact human health (2, 3). Nevertheless, the lower frequencies of electromagnetic waves and lower exposure times can be used to reduce these adverse effects (4).This method has been a candidate as an alternative disinfection process in industries to decrease the number of viable bacteria (5). Microwaves are categorized as a non-ionizing low frequency electromagnetic wave with frequencies between 300 MHz and 300 GHz (6). Many reports have been published on the lethal effects of microwave radiation on microorganisms (7, 8). Mechanisms underlying the lethal effect of microwave radiation on microorganisms are yet to be discovered. Some researchers hypothesized that electromagnetic waves can increase the target temperature and destroy life. However, non-thermal effects of electromagnetic waves, which are uniquely reported for microwaves, have been reported to be involved in lethal effects of electromagnetic waves (9).

On the other hand, several physicochemical methods have been developed to kill microorganisms (2, 10). Chemicals such as organic and inorganic compounds are widely used for disinfection process (11, 12). Moreover, the antimicrobial activity of different nanomaterials such as gold nanoparticles (AuNPs) has recently been reported (13). Hyperthermic gold nanoparticles under infrared radiation have been used for destruction of cancer cells (14). However, to the best of our knowledge, based on literature survey, the antimicrobial activity of AuNPs under electromagnetic radiation has not yet been studied and ought to be recognized.

In this study, AuNPs were synthesized with D-glucose and applied to augment the lethal effect of 2450 MHz electromagnetic radiation against S.aureus. The results showed that AuNPs significantly enhanced the lethal effect of electromagnetic radiation after a very little incubation time (5 s).

Materials and Methods Synthesis of gold nanoparticles

AuNPs were synthesized by a chemical method as previously has been reported (15). In this method, anhydrous D-glucose and soluble starch are used as reducing compound and a protecting agent, respectively. Forty µl of 1mM HAuCl4.3H2O solution (Merck, Germany) and 60 µl of 0.1 M D-glucose solution were added to 2 ml of 0.2%w pure starch (Sigma, USA) solution. Subsequently, 15 µl of sodium hydroxide (Merck, Germany) solution was added to the aforementioned solution mixed. The reaction mixture was incubated at room temperature for an hour.

In the next step, the prepared AuNPs was characterized by transmission electron microscopy (TEM) (EM 208 Philips), UV-visible spectrophotometry (Labomed Model UVD-2950 UV-VIS Double Beam PC Scanning spectrophotometer operated at a resolution of 2 min), and Energy-Dispersive Spectroscopy (EDS) (EM 208 Philips). For TEM experiment, aqueous suspension containing the AuNPs was dispersed ultrasonically, and a drop of suspension was located on carboncoated copper TEM grids and dried under an infrared lamp. Micrographs were achieved using a TEM (ZIESS 902A, Germany) operated at an accelerating voltage of 80 kV.

Finally, prepared AuNPs were separated by centrifugation (20000 ×g) for 45 min and washed three times with double distilled water. The pellet (0.8 mg) was re-dispersed in 1 ml distilled water (0.8 mg/ml) and homogenized in ultrasonic bath (5 min). This colloid was reserved in a screw capped container at 4°C for further experiments.

Antibacterial susceptibility test

Liquid serial dilution method using Müller–Hinton Broth (MHB) was used for evaluation of antibacterial activity of AuNPs against S.aureus ATCC 29737. MHB was further supplemented with serial concentrations of AuNPs (6.25, 12.5, 25, 50, 100, 400, 800 µg/mL). The inoculum was prepared from fresh culture of S.aureus. For this purpose, a loop full of the culture was suspended in sterile normal saline to 0.08-0.1 optical density (measured at 600 nm), which corresponded to about 5×107 colony-forming units per milliliter (Cfu/mL). An inoculum of approximately 5×105 Cfu/mL of test strain was inoculated in the prepared MHB as described above. The data are reported as Minimum Inhibitory Concentration (MIC), which was the lowest concentration of AuNPs that inhibited visible growth of test strain after 24 hr of incubation at 37°C (16).

Time-kill course assay

The antibacterial activity of sub-inhibitory concentration of AuNPs alone (50 µg/ml) and in combination with 2450 MHz electromagnetic radiation was evaluated against S.aureus using time-kill course assay. A microwave oven (Samsung M2330DN) operated at a low power (100 W) was used in this experiment. A suspension of S.aureus was prepared in sterile 0.9% NaCl. Aliquots of this bacterial suspension (1 mL) were dispensed in 8 tubes. Four test tubes containing the bacterial suspension were supplemented with 62.5 µl of the above AuNPs stock solution (50 µg/mL).

Then 62.5 µl of normal saline was added to other test tubes and these vessels were labeled as control tubes. In the next step, a test tube contained AuNPs and its control tube (with-out AuNPs) were exposed to microwave radiation in the microwave oven (100 W) for 5 s. This procedure was repeated for the other samples and control tubes for additional times (10, 15 and 20 s). The viable counts of bacteria in all the test tubes were determined before and after microwave treatment by standard Most Probable Number (MPN) method (17).

Results Synthesis and characterization

AuNPs were fabricated using D-glucose in soluble starch solution at room temperature. The appearance of purple color in reaction vessel confirms the formation of AuNPs (18). The inset in Figure 1 shows the reaction mixture before (vessel A) and after reaction with D-glucose for an hr at the room temperature (vessel B). The prepared colloid was characterized by UV-visible spectroscopy. The technique outlined above proved to be very useful for the analysis of nanoparticles (18).

UV-visible absorption spectrum of gold nano-particles fabricated by D-glucose. The inset in this figure shows the vessels containing the reaction mixture before (A) and after reaction with D-glucose for 1 hr at room temperature (B)

As illustrated in Figure 1, a strong absorption band with a maxima located at 530 nm was observed due to formation of AuNPs produced by the D-glucose. This peak is assigned to a surface plasmon, phenomenon that is well-documented for various metal nanoparticles with sizes ranging from 2 nm to 100 nm (19, 20).

Figure 2A shows the TEM image of the drop-coated film of the AuNPs and Figure 2B demonstrates their particle size distribution histogram. Figure 2A shows that small nanoparticles have been prepared with a diameter of less than 28 nm. Also, the mode of AuNPs size histogram is under 4 nm which is in accordance with 40% of all of the particles (Figure 2B). In the analysis of the AuNPs by EDS, the presence of elemental gold signal was confirmed in the sample (Figure 3). The Au nanocrystallites display an optical absorption band peaking at 2.15 keV which is typical of the absorption of metallic gold nanocrystallites (21).

Transmission electron micrograph (A) from a drop-coated film of prepared gold nanoparticles fabricated by D-glucose for 1 hr. The transmission electron micro-scopy image shows that small spherical nanoparticles. The particles size distribution histogram (B) shows that the size of generated nanoparticles was less than 28 nm and 40% of these nanoparticles were smaller than 4 nm

Energy-dispersive spectroscopy spectrum of prepared gold nanoparticles. Gold X-ray emission peak is labeled. Strong signals from the atoms in the nanoparticles are observed in spectrum and confirm the reduction of gold ions to gold nanoparticles

Antibacterial assay

The susceptibility of S.aureus ATCC 29737 against AuNPs was determined by serial broth dilution method. The obtained MIC was 100 µg/mL. The sub-MIC concentration of AuNPs (50 µg/ml) was selected to evaluate its enhancing effect on the lethal effect of certain electromagnetic wave (2450 MHz) generated in a microwave oven operated at low power (100 W).

Time-killed course study was selected for investigation of antibacterial activity of AuNPs alone and in combination with micro-wave radiation against S.aureus. The result of this experiment is shown in Figure 4. Rapid killing rate was observed for test strain in presence of AuNPs (Figure 4). Microbiological examination of the inoculated suspensions which contain AuNPs and treated in micro-wave oven (100 W), showed no viable cells after 5 s (Figure 4).

The viability of test stain (S.aureus) during treatment with low power microwave in the presence and absence of gold nanoparticles fabricated by D-glucose

In contrast, we detected considerable numbers of viable cells (about >104 Cfu/mL) in inoculated control tubes (without AuNPs) which incubated under microwave radiation at aforementioned time (5 s). This means that adding AuNPs to samples can enhance the antibacterial effect of microwave radiation that generated at microwave oven (100 W).

Discussion

It should be pointed out that low oven power (100 W) and sub-MIC concentration of AuNPs (50 µg/ml) were selected to guarantee that the effect produced in a short time exposure (5 s) was due to the combined method and not the effects of each factor alone. On the other hand, the effect observed in this condition could be due to the AuNPs-microwave radiation combination.

In a separate experiment, the temperatures of solutions which contain sub-inhibitory concentration of AuNPs (50 µg/ml) and treated by microwave at the same conditions, were also rapidly measured by a thermometer. The obtained temperature were 38°C, 39°C, 43°C and 47°C for samples which incubated for 5, 10, 15 and 20 s in microwave oven (100 W), respectively.

At the concentration tested (50 µg/ml), AuNPs significantly improved lethal effect of microwave radiation against S.aureus in 5 s. Longer incubation (10, 15, 20 s) of control samples (without AuNPs) in a microwave oven operated at 100 W led to gradual reduction of viable cells.

Anyhow, comparing the control samples, the application of AuNPs together with microwave radiation can significantly reduce (four times) the time required for complete destruction of test strain (Figure 4). In control tubes, time-kill course assay showed that the numbers of bacteria decreased to half the ratio in 5 s under microwave radiation which elevated temperature to 38°C. After 10 s, the viable counts decreased to about 100 Cfu/mL and temperature was 39°C. High killing rate was observed in ambient temperatures in microwave oven at 100 W. Therefore, non-thermal effects of microwave radiations may be involved in lethal phenomena. However, a marked increase in local temperature can also lead to the denaturation of proteins or disrupttion of organized biomolecules in the microorganisms. Further investigation should be carried out on the discovery of the possible mechanisms throughout the thermal and/or non-thermal effects in microwave radiation.

Conclusion

This investigation has described the enhancing effect of AuNPs on the lethal action of electromagnetic radiation generated in a microwave oven (100 W). Although many studies have been conducted to show the lethal effect of electromagnetic waves, but the antibacterial activity of microwave in the presence of AuNPs nanoparticles has never been investigated. This is a first report on the combined application of AuNPs with electromagnetic radiation for rapid killing of S. aureus in a short exposure time (5 s).

Electromagnetic radiations have been used as a killing agent (5) and the application of metal nanoparticles together with microwave radiation can reduce the time required to complete deactivation of microorganisms. This combination may be used for removing of contamination in medical devices like gauze or non-metal dentistry devices in short times (22).

Moreover, AuNPs are considered as inert and safe material (23). Therefore, this method may be selected as a rapid process for sterilization of heat sensitive drug substance or biological products in pharmaceutical industries. Further investigation should be performed in the future works on the stability of different chemicals during short time electromagnetic wave (2450 MHz) radiation process using a microwave oven operated at 100 W.

Acknowledgement

This work was supported by Faculty of Pharmacy, Tehran University of Medical Sciences, Tehran, Iran.

References Gier LJ Effects of ultrashort radio waves and ultraviolet light on microorganisms Trans Kans Acad Sci 1937 40 1-3 55 57 Garcia MM Brooks BW Stewart RB Dion W Trudel JR Ouwerkerk T Evaluation of gamma radiation levels for reducing pathogenic bacteria and fungi in animal sewage and laboratory effluxents Can J Vet Res 1987 51 3 285 289 Morgan WF Day JP Kaplan MI McGhee EM Limoli CL Genomic instability induced by ionizing radiation Radiat Res 1996 146 3 247 258 Leonard A Berteaud AJ Bruyere A An evaluation of the mutagenic, carcinogenic and teratogenic potential of microwaves Mutat Res 1983 123 1 31 46 Geveke DJ Brunkhorst C Fan X Radio frequency electric fields processing of orange juice Innovat Food Sci Emerg Tech 2007 8 4 549 554 Wiesbrock F Hoogenboom R Schubert US Microwave-assisted polymer synthesis: State-of-the-art and future perspective Macromol Rapid Commun 2004 25 1739 1764 Riddle MM Smialowicz RJ Rogers RR Micro-wave radiation (2450-MHz) potentiates the lethal effect of endotoxin in mice Health Phys 1982 42 3 335 340 Vela G R Wu JF Mechanism of lethal action of 2450-MHz radiation on microorganisms Appl Environ Microbiol 1979 37 3 550 553 Ohlsson T Bengtsson N Microwave technology and foods Adv Food Nutr Res 2001 43 65 140 Bialoszewski D Bocian E Bukowska B Czajkow-ska M Sokol-Leszczynska B Tyski S Antimicrobial activity of ozonted water Med Sci Monit 2010 16 9 T71 5 Bryce EA Spence D Roberts FJ An in-use evaluation of an alcohol-based pre-surgical hand disinfectant Infect Contr Hosp Epidemiol 2001 22 10 635 639 Rai M Yadav A Gade A Silver nanoparticles as a new generation of antimicrobials Biotechnol Adv 2009 27 1 76 83 Arshi N Ahmed F Kumar S Anwar MS Lu J Koo BH Microwave assisted synthesis of gold nanoparticles and their antibacterial activity against Escherichia coli (E.coli) Curr Appl Phys 2011 11 1 Supplement S360 S363 Huff TB Tong L Zhao Y Hansen MN Cheng JX Wei A Hyperthermic effects of gold nanorods on tumor cells Nanomedicine 2007 2 1 125 132 Raveendran P Fu J Wallen SL A simple and “green” method for the synthesis of Au, Ag, and Au-Ag alloy nanoparticles Green Chem 2006 8 1 34 38 Andrews JM Determination of minimum inhibitory concentrations J Antimicrob Chemother 2001 48 Suppl 1 5 16 Oblinger JL Koburger JA Understanding and teaching the most probable number technique J Milk Food Technol 1975 38 540 545 Shakibaie M Forootanfar H Mollazadeh-Moghaddam K Bagherzadeh Z Nafissi-Varcheh N Shahverdi AR Green synthesis of gold nanoparticles by the marine microalga Tetraselmis suecica Biotechnol Appl Biochem 2010 57 2 71 75 Henglein A Physicochemical properties of small metal particles in solution: “microelectrode” reactions, chemisorption, composite metal particles, and the atom-to-metal transition J Phys Chem B 1993 97 21 5457 5471 Sastry M Mayya KS Bandyopadhyay K pH dependent changes in the optical properties of carboxylic acid derivatized silver colloidal particles Colloid Surf A 1997 127 1-3 221 228 Singaravelu G Arockiamary S J Kumarb VG Govindaraju K Colloid Surf B Biointerfaces 2007 57 97 101 Cardoso VH Goncalves DL Angioletto E Dal-Pizzol F Streck EL Microwave disinfection of gauze contaminated with bacteria and fungi Indian J Med Microb 2007 25 4 428 429 Pissuwan D Cortie CH Valenzuela SM Cortie M Functionalized gold nanoparticles for controlling pathogenic bacteria Trends Biotechnol 2010 28 4 207 213